Qual técnica de aplicação de glaze de baixa fusão é melhor para criar uma superfície vítrea sobre a cerâmica Y-TZP?

Autores

  • Jean Soares Miranda Institute of Science and Technology - State University of São Paulo Julio de Mesquita Filho (UNESP), São José dos Campos, SP, Brazil
  • Natália Veloso Malta Federal University (UFJF), Juiz de Fora, MG, Brazil
  • Ronaldo Luís Almeida de Carvalho Braz Cubas Dental University, Mogi das Cruzes, SP, Brazil
  • Rodrigo Othávio de Assunção e Souza Federal University of Rio Grande do Norte (UFRN), Natal, RN, Brazil
  • João Paulo Barros Machado National Institute of Space Research (INPE), São José dos Campos, SP, Brazil
  • Fabíola Pessôa Pereira Leite Federal University (UFJF), Juiz de Fora, MG, Brazil

DOI:

https://doi.org/10.15448/1980-6523.2017.4.28749

Palavras-chave:

cerâmica de zircônia, nanofilme, tratamento de superfície.

Resumo

OBJETIVO: Avaliar a influência de dois tipos de aplicação de glaze de baixa fusão na superfície de uma cerâmica de zircônia estabilizada por ítrio (Y-TZP).
METODOLOGIA: Os espécimes de Y-TZP foram divididos em cinco grupos (n=5) de acordo com os tratamentos de superfície: controle (CO), nenhum tratamento foi realizado; aplicação de uma fina camada de glaze de baixa fusão pela técnica de pó/líquido (GPL); GPL seguida por condicinamento com ácido fluorídrico 10% (HF) (GPL-HF); aplicação de glaze spray (GS); GS seguido condicinamento com HF (GS-HF). Análise do ângulo de contato, aferição de rugosidade, difração de raios X, espectroscopia dispersiva de energia (EDS) e microscópio eletrônico de varredura (SEM) foram realizados.
RESULTADOS: Os exames ANOVA e Tukey revelaram que a GPL apresentou valores de ângulo de contato significativamente menores que os demais grupos (GPL: 50,31º; GPL-HF: 72,73º; GS-HF: 81,73º; CO: 96,48º; GS: 101,30º; p=0,001). GPL-HF apresentou uma rugosidade significativamente maior (Ra/Rq: 2658.0/3367.0 ηm; p=0,001) do que os outros grupos (GPL: 872.1/1162.0 ηm; GS-HF: 383.0/603.6 ηm; GS: 303.4/391.3 ηm; CO: 263.4/339.1 ηm). A análise de difracção de raios X apenas a fase tetragonal em todos os grupos. A análise EDS e SEM mostra uma quantidade grande de sílica na superfície GPL e GPL-HF.
CONCLUSÃO: A aplicação do glaze pela técnica de pó/líquido seguida do condicionamento com HF promoveu uma melhor superfície para a adesão micromecânica e química.

Referências

Moradabadi A, Roudsari SE, Yekta BE, Rahbar N. Effects of surface treatment on bond strength between dental resin agent and zirconia ceramic. Mater Sci Eng C Mater Biol Appl. 2014;34:311-7.

Bottino MA, Snellaert A, Bergoli CD, Özcan M, Bottino MC, Valandro LF. Effect of ceramic etching protocols on resin bond strength to a feldspar ceramic. OperDent. 2015;40:40-6.

Bottino MA, Bergoli C, Lima EG, Marocho SM, Souza RO, Valandro LF. Bonding of Y-TZP to dentin: effects of Y-TZP surface conditioning, resin cement type, and aging. Oper Dent. 2014;39:291-300.

Vanderlei A, Bottino MA, Valandro LF. Evaluation of resin bond strength to yttria-stabilized tetragonal zirconia and framework marginal fit: comparison of different surface conditionings. Oper Dent. 2014;39:50-63.

Amaral M, Belli R, Cesar PF, Valandro LF, Petschelt A, Lohbauer U. The potential of novel primers and universal adhesives to bond to zirconia. J Dent. 2014;42:90-8.

Dias de Souza GM, Thompson VP, Braga RR. Effect of metal primers on microtensile bond strength between zirconia and resin cements. J Prosthet Dent. 2011;105:296-303.

Cavalcanti AN, Foxton RM, Watson TF, Oliveira MT, Giannini M, Marchi GM. Y-TZP ceramics: key concepts for clinical application. Oper Dent. 2009;34:344-51.

Papia E, Zethraeus J, Ransbäck PÅ, Wennerberg A, Vult von Steyern P. Impaction-modified densely sintered yttria-stabilized tetragonal zirconium dioxide: methodology, surface structure, and bond strength. J Biomed Mater Res B Appl Biomater. 2012;100:677-84.

Maeda FA, Bello-Silva MS, de Paula Eduardo C, Miranda Junior WG, Cesar PF. Association of different primers and resin cements for adhesive bonding to zirconia ceramics. J Adhes Dent. 2014;16:261-5.

Özcan M, Bernasconi M. Adhesion to zirconia used for dental restorations: a systematic review and meta-analysis. J Adhes Dent. 2015;17:7-26.

Aboushelib MN, Mirmohamadi H, Matinlinna JP, Kukk E, Ounsi HF, Salameh Z. Innovations in bonding to zirconia-based materials. Part II: Focusing on chemical interactions. Dent Mater. 2009;25:989-93.

Pereira LL, Campos F, Dal Piva AM, Gondim LD, Souza RO, Özcan M. Can application of universal primers alone be a substitute for airborne-particle abrasion to improve adhesion of resin cement to zirconia? J Adhes Dent. 2015;17:169-74.

Yamamoto LT, Rodrigues VA, Dornelles LS, Bottino MA, Valandro LF, Melo RM. Low-Fusing Porcelain Glaze Application on 3Y-TZP Surfaces can Enhance Zirconia-Porcelain Adhesion. Braz Dent J. 2016;27:543-547.

Kelly JR. Dental ceramics: what is this stuff anyway? J AmDent Assoc 2008;139:4–7.

Thompson JY, Stoner BR, Piascik JR, Smith R.Adhesion/cementation to zirconia and other non-silicateceramics: where are we now? Dent Mater 2011;27:71–82.

Gargava S, Ram SM. Evaluation of Surface Conditioning of Zirconia and Its Effect on Bonding to Resin-Luting Agent. Journal of Contemporary Dentistry 2013; 3:7-10.

Inokoshi M, Kameyama A, De Munck J, Minakuchi S, Van Meerbeek B. Durable bonding to mechanically and/or chemically pre-treated dental zirconia. J Dent. 2013;41:170-9.

Martins AR, Gotti VB, Shimano MM, Borges GA, Gonçalves Lde S. Improving adhesion between luting cement and zirconia-based ceramic with an alternative surface treatment. Braz Oral Res. 2015;29:1-2.

Usumez A, Hamdemirci N, Koroglu BY, Simsek I, Parlar O, Sari T. Bond strength of resin cement to zirconia ceramic with different surface treatments. Lasers Med Sci. 2013;28:259-66.

Pozzobon JL, Pereira GKR, Wandscher VF, Dorneles LS, Valandro LF. Mechanical behavior of yttria-stabilized tetragonal zirconia polycrystalline ceramic after different zirconia surface treatments. Mater Sci Eng C Mater Biol Appl. 2017;77:828-35.

Şanlı S, Çömlekoğlu MD, Çömlekoğlu E, Sonugelen M, Pamir T, Darvell BW. Influence of surface treatment on the resin-bonding of zirconia. Dent Mater. 2015;31:657-68.

Wandscher VF, Prochnow C, Rippe MP, Dorneles LS, Callegari GL, Baldissara P, Scotti R, Valandro LF. Retentive Strength of Y-TZP Crowns: Comparison of Different Silica Coating Methods on the Intaglio Surfaces. Oper Dent. 2017;42:121-33.

Ntala P, Chen X, Niggli J, Cattell M. Development and testing of multi-phase glazes for adhesive bonding to zirconia substrates. J Dent. 2010 Oct;38:773-81.

Mota YA, Cotes C, Carvalho RF, Machado JPB, Leite FPP, Souza ROA, Özcan M. Monoclinic phase transformation and mechanical durability of zirconia ceramic after fatigue and autoclave aging. J Biomed Mater Res B Appl Biomater. 2017;105:1972-7.

Downloads

Publicado

2018-07-25

Edição

v. 32 n. 4 (2017)

Seção

Artigo Original

Licença

DIREITOS AUTORAIS
A submissão de originais para a Odonto Ciência implica na transferência, pelos autores, dos direitos de publicação. Os direitos autorais para os artigos publicados nesta revista são do autor, com direitos da revista sobre a primeira publicação. Os autores somente poderão utilizar os mesmos resultados em outras publicações indicando claramente a Odonto Ciência como o meio da publicação original.

LICENÇA CREATIVE COMMONS
Em virtude de ser uma revista de acesso aberto, permite-se o uso gratuito dos artigos em aplicações científicas e educacionais, desde que citada a fonte. De acordo com a Licença Creative Commons CC-BY 4.0, adotada pela Odonto Ciência o usuário deve respeitar os requisitos abaixo.

Você tem o direito de:
Compartilhar — copiar e redistribuir o material em qualquer suporte ou formato.
Adaptar — remixar, transformar e criar a partir do material para qualquer fim, mesmo que comercialmente.

Porém, somente de acordo com os termos seguintes:
Atribuição — Você deve dar o crédito apropriado, prover um link para a licença e indicar se mudanças foram feitas. Você deve fazê-lo em qualquer circunstância razoável, mas de maneira alguma que sugira que a Odonto Ciência apoia você ou o seu uso.
Sem restrições adicionais — Você não pode aplicar termos jurídicos ou medidas de caráter tecnológico que restrinjam legalmente outros de fazerem algo que a licença permita.

Avisos:
Você não tem de cumprir com os termos da licença relativamente a elementos do material que estejam no domínio público ou cuja utilização seja permitida por uma exceção ou limitação que seja aplicável.
Não são dadas quaisquer garantias. A licença pode não lhe dar todas as autorizações necessárias para o uso pretendido. Por exemplo, outros direitos, tais como direitos de imagem, de privacidade ou direitos morais, podem limitar o uso do material.

Para mais detalhes sobre a licença Creative Commons, siga o link no rodapé desta página eletrônica.