Marginal microleakage of class II composite resin restorations due to restorative techniques

Andreia A. Carvalho, Francine C. L. Moreira, Larissa M. Cunha, João Batista de Souza, Carlos Estrela, Lawrence G. Lopes

Abstract


Purpose: To evaluate the marginal microleakage of class II composite resin (CR) restorations due to restorative techniques.
Methods: Forty human extracted premolars were assigned to 4 groups (n=10). Class II cavities were prepared (4-mm wide, 2-mm axially, with the gingival margin located 1 mm beyond the cementum-enamel-junction), and the restorative adhesive system Prime & Bond 2.1/TPH3 (Dentsply) was used. CR was inserted by the oblique incremental technique (OIT) and cured in continuous exposure. The restoratives techniques were: group 1 (control): OIT; group 2: flowable resin (1 mm) applied in the gingival wall + OIT; group 3: OIT + three pre-cured spheres inserted in the first increment of CR; and, group 4: OIT + strip of fiberglass inserted in the first increment of CR. The specimens were subjected to a thermocycling regimen of 500 cycles (1 min at 5o-37o-55oC), coated with two layers of nail varnish up to 1 mm from the restoration margins, and immersed in 0.5% basic fuchsine solution for 24 h. The extension of dye penetration at the cervical wall (μm) was evaluated using an optic microscope at x40. Data were analyzed using analysis of variance (ANOVA) (α=0.05).
Results: The microleakage values were: G1: 370 μm ±241; G2: 398 μm ±354; G3: 205 μm ±119; and G4: 413 μm ±340. No statistically significant differences were found among the restorative techniques (P=0.081).
Conclusion: Marginal microleakage values were not influenced by the different restorative techniques tested.

Keywords


Composite resin; marginal microleakage; restorative technique

Full Text:

PDF


e-ISSN: 1980-6523

ISSN-L: 0102-9460

 

This journal is a member of, and subscribes to the principles of, the Committee on Publication Ethics (COPE) http://www.publicationethics.org


SJR (SCImago Journal & Country Rank) IMPACT FACTOR:

SCImago Journal & Country Rank

Licença Creative Commons

Except where otherwise noted, content of this journal is licensed under a Creative Commons Attribution 4.0 International license.

 

Editorial Policies of Brazilian Scientific Journals. Deposit availability: Blue .

 

Copyright: © 2006-2019 EDIPUCRS