Influência da contaminação com saliva na microinfiltração de restaurações de resina composta

Nihad Hasan Musa Hasan, Josiane Luzia Dias Damé, Flávio Fernando Demarco

Abstract



O objetivo deste estudo foi avaliar a influência da contaminação com saliva na microinfiltração
marginal de restaurações adesivas. Utilizaram-se 52 incisivos bovinos, sendo confeccionadas
cavidades Classe V (vestibular/lingual), com margens em dentina e esmalte. As
cavidades foram condicionadas com ácido fosfórico a 35% e divididas em quatro grupos.
G1 – sem contaminação, os demais grupos foram contaminados com saliva fresca por 15s,
sendo submetidos a diferentes tratamentos: G2 – secas com papel absorvente; G3 – lavadas
com água; G4 – recondicionadas por 10s. O sistema adesivo (Single Bond/3M ESPE) foi empregado
segundo recomendações do fabricante e as cavidades restauradas com compósito (Filtek
Z-250/3M ESPE). Após 24h as restaurações foram polidas e termocicladas (500 ciclos/5 e
55ºC/30s). Os dentes foram isolados, exceto as restaurações e a 1mm destas, imersos em fucsina
básica a 1% (24h) e lavados em água (24h). Foram seccionados e avaliados em lupa estereoscópica,
utilizando-se escores predeterminados, por dois examinadores calibrados. Os valores
obtidos foram submetidos à análise estatística (Kruskal-Wallis). A infiltração em dentina
foi significantemente maior que aquela observada em esmalte (p < 0,05). Nas margens em
dentina observou-se redução do selamento no G2 (p < 0,05). G3 e G4 restabeleceram o
selamento a níveis similares ao controle (G1). Nas margens em esmalte G1 apresentou selamento
similar ao G3 e ambos exibiram melhor selamento que G2 e G4 (p < 0,05), que foram similares.
Conclusões: dentro das limitações do estudo, verificou-se que a contaminação com saliva
após o condicionamento ácido interfere no selamento marginal de restaurações adesivas e os
tratamentos propostos apresentaram resultados diversos.

UNITERMOS: adesão; infiltração marginal; resina composta; saliva.

SUMMARY

The aim of this study was to evaluate the effect of saliva contamination on microleakage
of composite restorative. Fifty-two bovine incisives were selected, Class V cavities were
prepared (buccal/lingual), with margin in dentin and enamel. All cavities were 35% phosphoric
acid etched and divided in four groups. G1 – there was’nt contamination; in the remaining
groups, freshly collected saliva was used to contaminate for 15s and subjected to different
treatments: G2 – dried with absorvent papers; G3 – washed with water; G4 – reetched for
10s. The adhesive system (Single Bond/3M ESPE) was applied according to manufacturer
indications and the cavity was incrementally filled composite (Filtek Z-250/3M ESPE). The
teeth were polish and thermocycled (500 cycles/5 and 55o C/30s), isolated and immersed in
1% basic fuchsin solution (24h). After washing in tap water (24h), each tooth was sectioned
and the dye penetration was evaluated under magnification (40) by 2 calibrated examiners,
using standard scores. Data were submitted to a nonparametric Kruskal-Wallis test with a
confidence level of 95%. The dye penetration was higher in dentin than in enamel (p < 0.05). In dentin margins there was higher microleakage in G2 (p < 0.05), G3 and G4 have achieved
similar values to control G1. In enamel margins, G1 exhibited similar results than G3 and
both exhibited better sealing performances than G2 and G4 (p < 0.05), which were similar.
Conclusions: Within the limitations of the study, it was possible to verify that saliva
contamination impair the marginal quality of composite restorative and the treatments used
after contamination showed different results.

UNITERMS: adhesion; composite resin; microleakage; saliva.

Full Text:

PDF


e-ISSN: 1980-6523

ISSN-L: 0102-9460

 

This journal is a member of, and subscribes to the principles of, the Committee on Publication Ethics (COPE) http://www.publicationethics.org


SJR (SCImago Journal & Country Rank) IMPACT FACTOR:

SCImago Journal & Country Rank

Licença Creative Commons

Except where otherwise noted, content of this journal is licensed under a Creative Commons Attribution 4.0 International license.

 

Editorial Policies of Brazilian Scientific Journals. Deposit availability: Blue .

 

Copyright: © 2006-2019 EDIPUCRS